Tabelli tad-Data
Kompożizzjoni Kimika:
2205 stainless steel coiled tubu kompożizzjoni kimika
| Cr | Ni | Mo | Co | Nb (+Ta) | Ti | V | W | Cu | C | Mn | N | Si | P | S | Fe | Al | |
| Min | 22.00 | 4.50 | 3.00 | 0.14 | 0.20 | ||||||||||||
| Max | 23.00 | 6.50 | 3.50 | 0.03 | 0.20 | 0.70 | 0.03 | 0.02 | Bal |
Proprjetajiet mekkaniċi:
2205 stainless steel coiled tubu kompożizzjoni kimika
| 0.2% Stress tal-Prova | 450 N/mm2 | 65ksi |
| Saħħa tat-tensjoni | 655 N/mm2 | 95ksi |
| Titwil, 5.65√S0 | 25% | |
| Tnaqqis taż-żona | 45% | |
| Ebusija (Brinell) | <270 | |
| Qawwa tal-Impatt (Temperatura tal-Kamra) | 80J (av) | |
| Qawwa tal-Impatt (-46 ° C): Lonġitudinali | <100mm 80J | |
| 100-260mm 45J (35J min) | ||
| > 260mm Għal informazzjoni biss | ||
| Qawwa tal-Impatt (-46oC): Trasversali | 50-260mm 45J (35J min) | |
| > 260mm Għal informazzjoni biss | ||
Noti:
2205 stainless steel coiled tubu kompożizzjoni kimika
- L-ittestjar għandu jsir skont ASTM A370 jew EN ISO 6892-1 (tensjoni), EN ISO 6506-1 (ebusija)
- Proprjetajiet minimi kkwotati (ittestjati f'temperatura ambjentali f'direzzjoni lonġitudinali)
- Ittestjar imwettaq fuq kull tidwib ta 'materjal għal kull lott ta' trattament tas-sħana
- L-ebusija għandha tkun skont NACE MR 1075
- Test tal-korrużjoni ASTM G48A (f'25°C) L-ebda pitting u < 3.0g/m2telf ta 'piż
- Kontenut tal-ferrite 40-55%
- Mikrostruttura ċċertifikata ħielsa minn karburi tal-konfini tal-qamħ, fażijiet sigma, chi u laves
Proprjetajiet fiżiċi: 2205 stainless steel coiled tubu kompożizzjoni kimika
| Densità (Kg/m3) | 7810 |
| Permeabilità manjetika (20°C) | <50 |
| Modulu ta' Young (kN/mm2) | 190 |
| Reżistenza Elettrika Speċifika, 20°C (µΩ.m) | 0.85 |
| Koeffiċjent medju ta 'espansjoni termali, 20-300 ° C (m/m/oC) | 11 x 10-6 |
| Sħana Speċifika, 20°C (J/kg.K) | 400 |
| Konduttività termali, 20°C (W/mK) |